PPA 9G22750 H
0
- Properties:Fillercarbon fiber reinforced material50%filler by weight
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO1183 | 1.49 g/cm³ | |
| Water absorption rate | ISO62 | 1.3 % | |
| Moisture content | ISO960 | <2000 ppm | |
| density | ISO 1183 | 1.49 g/cm³ | |
| Water absorption rate | ISO 62 | 1.3 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL94 | HB | |
| UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO527-2/5 | 35000 MPa | |
| Tensile stress | ISO527-2/5 | 280 MPa | |
| Tensile modulus | ISO 527-2/5 | 35000 MPa | |
| Tensile stress | ISO 527-2/5 | 280.0 MPa | |
| Impact strength of cantilever beam gap | ISO 180/1A | 10 kJ/m² | |
| Thermal performance | ISO 75-2/A | 285 °C | |
| Melting Temperature | ISO 11357 | 315 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO180/1A | 10 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO75-2/A | 285 °C | ||
| flammability | UL 94 | HB | |
| UL 94 | HB | ||
| melting temperature | ISO11357 | 315 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.