Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.20 g/cm³ |
| melt mass-flow rate | | ISO1133 | 6.0 g/10min |
| Shrinkage rate | | | 0.50 % |
| Water absorption rate | | ISO62 | 0.15 % |
| density | | ISO 1183 | 1.20 g/cm³ |
| | ISO 1133 | 6.0 g/10 min |
| Shrinkage rate | | ISO 2557 | 0.50 % |
| Water absorption rate | | ISO 62 | 0.15 % |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | ASTMD1003 | 80.0到90.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| Burning wire flammability index | | IEC60695-2-12 | 870 °C |
| Heat distortion temperature | Test Condition | Test Method | Test Result |
|---|
| optical performance | | ASTM D1003 | 80.0-90.0 % |
| other | | UL 94 | HB |
| other | | UL 94 | HB |
| Burning wire flammability index | | IEC 60695-2-12 | 870 °C |
| Electrical performance | | IEC 60112 | 250 V |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ISO 527-2/5 | 58.0 MPa |
| Tensile stress | | ISO 527-2/5 | 52.0 MPa |
| Tensile strain | | ISO 527-2/5 | 8.0 % |
| Tensile strain | | ISO 527-2/5 | 93.0 % |
| Bending stress | | ISO 178 | 90.0 MPa |
| Charpy Notched Impact Strength | | ISO 179/1eA | 19.0 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 15.0 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 60.0 kJ/m² |
| Tensile modulus | | ISO527-2/5 | 2350 MPa |
| Tensile stress | | ISO527-2/5 | 58.0 MPa |
| Tensile stress | | ISO527-2/5 | 52.0 MPa |
| Tensile strain | Yield | ISO527-2 | 8.0 % |
| Tensile strain | | ISO527-2/5 | 93 % |
| Bending stress | | ISO178 | 90.0 MPa |
| Tensile modulus | | ISO 527-2/5 | 2350 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/B | 19 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 15 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 60 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| CTI | | IEC60112 | 250 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO306/B | 145 °C |
| | ISO75-2/B | 144 °C |
| | ISO 75-2/B | 144 °C |
| | ISO 306/B | 145 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.