Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | g/cm³ | 1.36 1.36 |
| Shrinkage rate | | % | 0.70 0.70 |
| Shrinkage rate | | % | 0.20 0.20 |
| Water absorption rate | | % | 1.3 1.3 |
| Water absorption rate | | % | 2.0 2.0 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | | 120 107 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | | HB HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | MPa | 9600 6000 |
| Tensile stress | Break | MPa | 170 110 |
| Tensile strain | Break | % | 3.1 5.3 |
| Flexural modulus | | MPa | 8200 5000 |
| Bending stress | | MPa | 250 160 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | kJ/m² | 11 19 |
| Impact strength of simply supported beam without notch | | kJ/m² | 70 85 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ohms·cm | 2E+15 7E+13 |
| dielectric strength | | kV/mm | 42 40 |
| dielectric constant | | | 3.30 3.60 |
| Dissipation Factor | | | 0.022 0.12 |
| CTI | | V | 550 550 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | °C | 217 -- |
| | °C | 203 -- |
| | cm/cm/°C | 3.1E-05 3.1E-05 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.