PA6 K224-G6-FC BK00001 DSM Additive Manufacturing
0
- Properties:Fillerglass fiber reinforced material30%filler by weight
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.35 g/cm³ | |
| Shrinkage rate | ISO 294-4 | 0.90 % | |
| ISO 294-4 | 0.30 % | ||
| Water absorption rate | ISO 62 | 6.3 % | |
| ISO 62 | 1.9 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 11 kJ/m² | |
| ISO 179/1eA | 12 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO 179/1eU | 75 kJ/m² | |
| ISO 179/1eU | 90 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 9500 MPa | |
| tensile strength | Break | ISO 527-2 | 180 MPa |
| Tensile strain | Break | ISO 527-2 | 3.5 % |
| Flexural modulus | ISO 178 | 8600 MPa | |
| bending strength | ISO 178 | 235 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dissipation Factor | IEC 60250 | 5E-03 | |
| IEC 60250 | 0.015 | ||
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V | |
| Surface Resistivity | IEC 60093 | -- ohms | |
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 30 kV/mm | |
| relative permittivity | IEC 60250 | 3.50 | |
| IEC 60250 | 3.30 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/B | 220 °C | |
| ISO 75-2/A | 200 °C | ||
| melting temperature | ISO 11357-3 | 220 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 2E-05 cm/cm/°C | |
| ISO 11359-2 | 7E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.