Technical Data Sheet
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1A/1 | 13000 Mpa |
| tensile strength | | ISO 527-2/1A/5 | 130 Mpa |
| Tensile strain | | ISO 527-2/1A/5 | 1.8 % |
| Flexural modulus | | ISO 178 | 12000 Mpa |
| Charpy Notched Impact Strength | | ASTM D256/ISO 179 | 35 kg·cm/cm(J/M)ft·lb/in |
| elongation at break | | ASTM D638/ISO 527 | 1.8 % |
| Tensile modulus | | ASTM D638/ISO 527 | 13000 kg/cm²(MPa)[Lb/in²] |
| elongation | | ASTM D638/ISO 527 | 130 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 35 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | >1.0E+16 ohms |
| Volume resistivity | | IEC 60093 | >1.0E+16 ohms·cm |
| dielectric strength | | IEC 60243-1 | 36 KV/mm |
| relative permittivity | | IEC 60250 | 4.00 |
| relative permittivity | | 内部方法 | 4.16 |
| Dissipation Factor | | IEC 60250 | 0.031 |
| Dissipation Factor | | 内部方法 | 5E-03 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 3 |
| Surface Resistivity | | ASTM D257/IEC 60093 | >1.0E+16 Ω |
| arc resistance | | ASTM D495/IEC 60112 | 36 |
| Volume resistivity | | ASTM D257/IEC 60093 | >1.0E+16 Ω.cm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 1.62 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 265 °C |
| melting temperature | | ISO 11357-3 | 335 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 3E-06 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 7E-05 cm/cm/°C |
| Combustibility (rate) | | UL 94 | v-0 |
| Heat distortion temperature | | ASTM D648/ISO 75 | 265 ℃（℉） |
| Linear coefficient of thermal expansion | | ASTM D696/ISO 11359 | 3.0E-6 mm/mm.℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.