Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.13 g/cm³ |
| Water absorption rate | | ISO62 | 11 % |
| Water absorption rate | | ISO62 | 2.9 % |
| viscosity number | | ISO307 | 185 cm³/g |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Hot filament ignition temperature | | IEC60695-2-13 | 700 °C |
| burning rate | | FMVSS302 | 0.0 mm/min |
| UL flame retardant rating | | UL94 | HB |
| Burning wire flammability index | | IEC60695-2-12 | 800 °C |
| Burning wire flammability index | | IEC60695-2-12 | 750 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 825 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Nominal tensile fracture strain | | ISO527-2/1A/50 | 40 % |
| Flexural modulus | | ISO178 | 2800 MPa |
| Bending stress | | ISO178 | 105 MPa |
| Tensile modulus | | ISO527-2/1A/1 | 3100 MPa |
| Tensile stress | Yield | ISO527-2/1A/50 | 80.0 MPa |
| Tensile strain | Yield | ISO527-2/1A/50 | 4.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 4.5 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 6.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC60093 | 1E+15 ohms·cm |
| CTI | | IEC60112 | 600 V |
| Surface Resistivity | | IEC60093 | 1E+12 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/Bf | 170 °C |
| | ISO75-2/Af | 55.0 °C |
| vicat | | ISO306/B50 | 195 °C |
| melting temperature | | ISO11357 | 220 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.