PPO SE1GFN1-701 SABIC EU

Form：Granules | Grade：Injection grade

Properties:

enhanceGlass fiber reinforcedFlame retardantHigh mobilityHigh temperature resistan

Typical Applications:

Electronic communication accessoriesElectronic communication accessoriesHousehold appliancesHousehold appliancesAutomotive interior partsSports EquipmentAbove water

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electronic communication accessories \| Electronic communication accessories \| Household appliances \| Household appliances \| Automotive interior parts \| Sports Equipment \| Above water
Properties:	enhance \| Glass fiber reinforced \| Flame retardant \| High mobility \| High temperature resistan

Certificates

No Data...

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5 mm	UL 94	V-1
Extreme Oxygen Index		ASTM D2863	34	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	Break, 50.0 mm Span	ASTM D790	119	Mpa
Bending modulus	50.0 mm Span	ASTM D790	3990	Mpa
elongation	Break	ASTM D638	5.0	%
tensile strength	Break	ASTM D638	74.0	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			105 to 110	°C
drying time			3.0 to 4.0	hr
Suggested maximum moisture content			0.020	%
Suggested injection volume			30 to 70	%
Temperature at the rear of the barrel			250 to 300	°C
Temperature in the middle of the barrel			260 to 305	°C
Temperature at the front of the material cylinder			270 to 310	°C
Spray nozzle temperature			280 to 310	°C
Processing (melt) temperature			280 to 310	°C
Mold temperature			75 to 105	°C
Back pressure			0.300 to 0.700	Mpa
Screw speed			20 to 100	rpm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
RTI		UL 746	110	°C
RTI Imp		UL 746	105	°C
RTI Elec		UL 746	110	°C
Vicat softening temperature		ASTM D15254	147	°C
Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	131	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium, 23°C	ASTM D570	0.22	%
Water absorption rate	Water absorption rate	24 hr	ASTM D570	0.070	%
Shrinkage rate	3.20 mm，Flow	Internal Method	0.30 - 0.50	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Hot wire ignition		UL 746	PLC 1
High voltage arc tracing rate		UL 746	PLC 4
High arc combustion index		UL 746	PLC 2
Compared to the anti leakage trace index		UL 746	PLC 2
Dissipation factor	1 MHz	ASTM D150	1.6E-3
	Dissipation factor	60 Hz	ASTM D150	1.7E-3
	Dissipation factor	Dissipation factor	50 Hz	ASTM D150	1.7E-3
Dielectric constant	1 MHz	ASTM D150	3.00
	Dielectric constant	50 kHz	ASTM D150	3.00
	Dielectric constant	Dielectric constant	60 Hz	ASTM D150	3.00
Volume resistivity		ASTM D257	1.0E+15	ohms·cm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	L -Sale	ASTM D785	104

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.