PC 1201-15 LG CHEM KOREA

100

Form：Granules | Grade：Injection grade

Properties:

transparentwear resistantFood contact complianceLow viscosityGood demolding performanc

Typical Applications:

ToyFood containerschipNon specific foodbottleToyDisposable tablewareShieldchipbottle

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Toy \| Food containers \| chip \| Non specific food \| bottle \| Toy \| Disposable tableware \| Shield \| chip \| bottle
Properties:	transparent \| wear resistant \| Food contact compliance \| Low viscosity \| Good demolding performanc

Certificates

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
Refractive index		ASTM D542	1.586
transmissivity		ASTM D1003	89.0	%
turbidity		ASTM D1003	0.70to1.5	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	850	J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D256	NoBreak
Dart impact	23°C,3.20mm,TotalEnergy	ASTM D3763	87.0	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.50mm	UL 94	V-2
	UL flame retardant rating	1.6mm	UL 94	V-2
		UL flame retardant rating	2.5mm	UL 94	V-2
		UL flame retardant rating	UL flame retardant rating	2.7mm	UL 94	V-2
Hot filament ignition temperature	2.0mm	IEC 60695-2-13	850	°C
Extreme Oxygen Index		ASTM D2863	26	%
Average degree of combustion		ASTM D635	3	CM
UL flame retardant rating	3.0mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus		ASTM D790	2410	Mpa
bending strength		ASTM D790	96.0	Mpa
Wear resistance	雾度变化	ASTM D1004	45	%
Tensile modulus		ASTM D638	2340	Mpa
tensile strength	Yield,23°C	ASTM D638	60.0	Mpa
tensile strength	tensile strength	Break	ASTM D638	71.0	Mpa
elongation	Yield	ASTM D638	6.0	%
elongation	elongation	Break	ASTM D638	150	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Annealed,4.00mm	ASTM D648	143	°C
	Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ASTM D648	127	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed,4.00mm	ASTM D648	140	°C
Vicat softening temperature		ASTM D15256	148	°C
Ball pressure temperature		IEC 60598-1	>125	°C
Linear coefficient of thermal expansion	MD：-40to82°C	ASTM D696	6.8E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792	1.20	g/cm³
melt mass-flow rate	300°C/1.2kg	ASTM D1238	15	g/10min
Shrinkage rate	MD	ASTM D955	0.50-0.70	%
Water absorption rate	23°C,24hr	ASTM D570	0.15	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ASTM D570	0.32	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity	23°C	ASTM D257	2E+17	ohms·cm
Dielectric strength		ASTM D149	17	KV/mm
Dielectric constant	60Hz	ASTM D150	3.00
Dissipation factor	60Hz	ASTM D150	1E-03
Compared to the anti leakage trace index	2.00mm	IEC 60112	PLC 2
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Sale	ASTM D785	73
Rockwell hardness	Rockwell hardness	R-Sale	ASTM D785	118

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.