POM 127UV DUPONT USA

Form：Granules | Grade：Injection grade

Properties:

High temperature resistanFlame retardantenhance

Typical Applications:

Medical supplies

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Medical supplies
Properties:	High temperature resistan \| Flame retardant \| enhance

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C	ISO 180/1A	13	kJ/m²
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	11	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	15	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	350	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	400	kJ/m²
Impact strength of cantilever beam gap	-40°C	ISO 180/1A	11	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning rate	1.00mm	ISO 3795	28	mm/min
UL flame retardant rating	0.8mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	0.8mm	IEC 60695-11-10,-20	HB
FMVSS flammability		FMVSS302	B
Fogging-G-value	condensate	ISO 6452	1.5E-04	g
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2	3000	Mpa
tensile strength	Yield	ISO 527-2	70.0	Mpa
Tensile strain	Yield	ISO 527-2	23	%
Nominal tensile fracture strain		ISO 527-2	45	%
Bending modulus		ISO 178	2700	Mpa
bending strength	3.5%Strain	ISO 178	80.5	Mpa
bending strength	bending strength	--	ISO 178	72.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
AnnealingTime-Optional			30.0	min/mm
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	160	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	93.0	°C
Vicat softening temperature		ISO 306/B50	160	°C
Melting temperature		ISO 11357-3	178	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	1.2E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	1.1E-04	cm/cm/°C
AnnealingTemperature			160	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.42	g/cm³
melt mass-flow rate	190°C/2.16kg	ISO 1133	2.4	g/10min
Melt Volume Flow Rate (MVR)	190°C/2.16kg	ISO 1133	1.90	cm3/10min
Shrinkage rate	TD	ISO 294-4	1.9	%
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	2.1	%
Water absorption rate	23°C,24hr	ISO 62	0.50	%
	Water absorption rate	Saturation,23°C,2.00mm	ISO 62	1.2	%
	Water absorption rate	Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.30	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		IEC 60093	1E+13	ohms·cm
Relative permittivity	100Hz	IEC 60250	3.50
Relative permittivity	Relative permittivity	1MHz	IEC 60250	3.40
Compared to the anti leakage trace index		IEC 60112	PLC 0
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Sale	ISO 2039-2	92
Rockwell hardness	Rockwell hardness	R-Sale	ISO 2039-2	120
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
Emission		VDA275	<8.00	mg/kg
EmissionofOrganicCompounds		VDA277	16.0	µgC/g
Odor		VDA270	3.00

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.