PA66 ST801 NC010 DUPONT USA

126

Form：Granules | Grade：Toughened grade

Properties:

High impact resistance

Typical Applications:

Fitness equipmentBottle capAutomotive sector

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Fitness equipment \| Bottle cap \| Automotive sector
Properties:	High impact resistance

Certificates

Technical Data Sheet

Filling analysis	Test Condition	Test Method	Test Result	Test Unit
Top out temperature			190	°C
impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	20	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C, Partial Break	ISO 179/1eA	70	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	--
Impact strength of cantilever beam gap	-40°C	ISO 180/1A	20	kJ/m²
	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	15	kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	80	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning rate	1.00 mm	ISO 3795	< 100	mm/min
UL flame retardant rating		UL 94	HB
UL flame retardant rating	UL flame retardant rating		UL 94	HB
Extreme Oxygen Index		ISO 4589-2	20	%
FMVSS combustion rate		FMVSS 302	B
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2	2000	Mpa
tensile strength	50% Strain	ISO 527-2	49.0	Mpa
Tensile strain	Break	ISO 527-2	> 50	%
Tensile creep modulus	1 hr	ISO 899-1	--	Mpa
Tensile creep modulus	Tensile creep modulus	1000 hr	ISO 899-1	--	Mpa
Bending modulus		ISO 178	1800	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			80	°C
Drying time - hot air dryer			2.0 to 4.0	hr
Suggested maximum moisture content			0.20	%
Processing (melt) temperature			280 to 300	°C
Melt Temperature, Optimum			290	°C
Mold temperature			50 to 100	°C
Mold Temperature, Optimum			80	°C
Maintain pressure			50.0 to 100	Mpa
Maintain pressure	Maintain pressure	Drying Recommended		yes
Hold Pressure Time			4.00	s/mm
Maximum Screw Tangential Speed			18	m/min
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	157	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	63.0	°C
Glass transition temperature		ISO 11357-2	75.0	°C
Vicat softening temperature		ISO 306/B50	205	°C
Melting temperature		ISO 11357-3	262	°C
Linear coefficient of thermal expansion	Flow : 23 to 55°C	ASTM E831	1.4E-4	cm/cm/°C
	Linear coefficient of thermal expansion	Flow	ISO 11359-2	1.4E-4	cm/cm/°C
		Linear coefficient of thermal expansion	Flow : -40 to 23°C	ISO 11359-2	1.1E-4	cm/cm/°C
			Linear coefficient of thermal expansion	Flow : 55 to 160°C	ISO 11359-2	1.6E-4	cm/cm/°C
				Linear coefficient of thermal expansion	Across Flow : 23 to 55°C	ASTM E831	1.3E-4	cm/cm/°C
					Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	1.3E-4	cm/cm/°C
						Linear coefficient of thermal expansion	Across Flow : -40 to 23°C	ISO 11359-2	1.1E-4	cm/cm/°C
						Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 55 to 160°C	ISO 11359-2	1.3E-4	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.07	g/cm³
Shrinkage rate	横向Flow	ISO 294-4	1.4	%
Shrinkage rate	Shrinkage rate	Flow	ISO 294-4	1.8	%
Water absorption rate	24 hr, 23°C	ISO 62	1.1	%
	Water absorption rate	Saturation, 23°C, 2.00 mm	ISO 62	6.5	%
	Water absorption rate	Water absorption rate	Equilibrium, 23°C, 2.00 mm, 50% RH	ISO 62	2.0	%
Stickiness		ISO 307	130	cm³/g
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 62631-3-2	--	ohms
Volume resistivity		IEC 62631-3-1	> 1.0E+13	ohms·m
Dielectric strength		IEC 60243-1	25	KV/mm
Relative permittivity	1 MHz	IEC 62631-2-1	3.30
Relative permittivity	Relative permittivity	100 Hz	IEC 62631-2-1	3.50
Dissipation factor	100 Hz	IEC 62631-2-1	5.0E-3
Dissipation factor	Dissipation factor	1 MHz	IEC 62631-2-1	0.010
Compared to the anti leakage trace index		IEC 60112	PLC 0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.