PA66 164 NT RADICI SUZHOU

Form：Granules

Typical Applications:

Laptop caseWire and cable applicationsFasteners

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:

Laptop case | Wire and cable applications | Fasteners

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning wire flammability index	2.0mm	IEC 60695-2-12	800	°C
Burning wire flammability index	Burning wire flammability index	1.0mm	IEC 60695-2-12	750	°C
UL flame retardant rating	0.8mm	UL 94	V-2
UL flame retardant rating	UL flame retardant rating	0.40mm	UL 94	V-2
Burning rate		FMVSS302	0.0	mm/min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	110	Mpa
Bending modulus		ISO 178	2900	Mpa
Nominal tensile fracture strain		ISO 527-2/1A/50	35	%
Tensile strain	Yield	ISO 527-2/1A/50	4.5	%
tensile strength	Yield	ISO 527-2/1A/50	85.0	Mpa
Tensile modulus		ISO 527-2/1A/1	3100	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/Af	70.0	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/Bf	200	°C
Melting temperature		ISO 11357	260	°C
Vicat softening temperature		ISO 306/B50	240	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	2.1	%
Water absorption rate	Water absorption rate	Saturation,23°C,2.00mm	ISO 62	8.9	%
Shrinkage rate	MD	ISO 294-4	1.8	%
Shrinkage rate	Shrinkage rate	TD	ISO 294-4	1.9	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index		IEC 60112	PLC 0
Volume resistivity		IEC 60093	1E+15	ohms·cm
Surface resistivity		IEC 60093	1E+12	ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.