Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Thermosetting mixed viscosity | | ASTMD4878 | 4050 cP |
| stripping time | | | 1400 min |
| GelTime | | ASTMD2971 | 40.0到60.0 min |
| | | 按重量计算的混合比:100,按容量计算的混合比:100 |
| | | 按重量计算的混合比:16,按容量计算的混合比:30 |
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD4669 | 1.59 g/cm³ |
| Shrinkage rate | | ASTMD2566 | 0.050到0.10 % |
| Weight Percubicinch | | | 26 g |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ASTMD2240 | 88 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTMD638 | 2140 MPa |
| tensile strength | | ASTMD638 | 44.8 MPa |
| elongation | Break | ASTMD638 | 1.7 % |
| Flexural modulus | | ASTMD790 | 2250 MPa |
| bending strength | | ASTMD790 | 50.7 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Suspended wall beam without notch impact strength | | ASTMD256 | 42 J/m |
| Impact strength of cantilever beam gap | | ASTMD256 | 31 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | ASTMD150 | 3.60 |
| dielectric constant | | ASTMD150 | 3.30 |
| Dissipation Factor | | ASTMD150 | 0.022 |
| Volume resistivity | | ASTMD257 | 7.3E+13 ohms·cm |
| dielectric strength | | ASTMD149 | 25 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| thermal conductivity | | | 0.39 W/m/K |
| Service | | | 85 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare