Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Thermosetting mixed viscosity | | ASTM D4878 | 670 cP |
| stripping time | | | 4.0to6.0 min |
| GelTime | | ASTM D2971 | 20.0 min |
| Thermosetting components | | | 按重量计算的混合比:100.按容量计算的混合比:100 |
| Thermosetting components | | | 按重量计算的混合比:100.按容量计算的混合比:100 |
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D4669 | 1.05 g/cm³ |
| Shrinkage rate | | ASTM D2566 | 0.20to0.30 % |
| Weight Percubicinch | | | 17 g |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | Shore A | ASTM D2240 | 65 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ThermalShockTest | | | Pass |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 4.14 MPa |
| tensile strength | | ASTM D638 | 6.21 MPa |
| elongation | Break | ASTM D638 | 500 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 无断裂 |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tear strength | | ASTM D624 | 14.4 kN/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 8.9E+16 ohms·cm |
| dielectric strength | | ASTM D149 | >14 kV/mm |
| dielectric constant | | ASTM D150 | 2.50 |
| dielectric constant | | ASTM D150 | 2.40 |
| Dissipation Factor | | ASTM D150 | 0.023 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Usage temperature | | | 80 °C |
| thermal conductivity | | | 0.23 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.