'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PBT VX5011-7001 SABIC INNOVATIVE SHANGHAI
146
Form：Granules | Grade：Injection grade
Properties:
Low warpageAging resistanceFiller: Glass fiber reinf10%Filler by weight10%Filler by weight
Typical Applications:
chipElectronic and Electrical Applications
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | chip | Electronic and Electrical Applications |
| Properties: | Low warpage | Aging resistance | Filler: Glass fiber reinf | 10% | Filler by weight | 10% | Filler by weight |
Certificates
No Data...
Technical Data Sheet
| Filling analysis | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Melt viscosity | 260°C,1500sec^-1 | ISO 11443 | 145 | Pa·s |
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
| -30°C | ISO 179/1eA | 4.0 | kJ/m² | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 37.0 | J |
| 23°C | ISO 180/1U | 40 | kJ/m² | |
| -30°C | ISO 180/1U | 30 | kJ/m² | |
| 23°C | ASTM D4812 | 480 | J/m | |
| ISO 180/1A | 6.0 | kJ/m² | ||
| -30°C | ASTM D4812 | 470 | J/m | |
| 0°C | ISO 180/1A | 5.0 | kJ/m² | |
| -30°C | ISO 180/1A | 5.0 | kJ/m² | |
| 0°C | ASTM D256 | 47 | J/m | |
| 23°C | ASTM D256 | 47 | J/m | |
| -30°C | ASTM D256 | 47 | J/m | |
| 23°C | ISO 179/1eU | 40 | kJ/m² | |
| -30°C | ISO 179/2U | 40 | kJ/m² | |
| 23°C | ISO 179/1eA | 4.0 | kJ/m² | |
| ISO 179/2C | 6.0 | kJ/m² | ||
| -30°C | ISO 179/1eU | 30 | kJ/m² | |
| ISO 179/2C | 6.0 | kJ/m² | ||
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| Extreme Oxygen Index | ISO 4589-2 | 21 | % | |
| Burning wire flammability index | 3.00mm | IEC 60695-2-12 | 850 | °C |
| 1.00mm | IEC 60695-2-12 | 750 | °C | |
| UL flame retardant rating | 1.60mm | UL 94 | HB | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Fracture bending strain | ISO 178 | 5.0 | % | |
| Taber abraser | 1000Cycles,1000g,CS-17Wheel | Internal Method | 54.0 | mg |
| --3 | ASTM D638 | 4600 | Mpa | |
| yield | ASTM D638 | 90.0 | Mpa | |
| ISO 527-2/5 | 95.0 | Mpa | ||
| crack | ASTM D638 | 90.0 | Mpa | |
| ISO 527-2/5 | 95.0 | Mpa | ||
| yield | ASTM D638 | 3.0 | % | |
| ISO 527-2/5 | 3.0 | % | ||
| Yield, 50.0mm span | ASTM D790 | 126 | Mpa | |
| --11 | ISO 178 | 130 | Mpa | |
| --10 | ISO 178 | 140 | Mpa | |
| --9 | ISO 178 | 4000 | Mpa | |
| 50.0mm span | ASTM D790 | 3600 | Mpa | |
| crack | ISO 527-2/5 | 3.0 | % | |
| ASTM D638 | 3.0 | % | ||
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| 1.8MPa, unannealed, 64.0mm span of | ISO 75-2/Af | 115 | °C | |
| Ball Pressure Test | 125°C | IEC 60695-10-2 | Pass | |
| Flow: -40 to 40 ° C | ASTME831 | 4E-05 | cm/cm/°C | |
| ISO 11359-2 | 3.7E-05 | cm/cm/°C | ||
| Flow: 23 to 80 ° C | 23to80℃ | ISO 11359-2 | 4E-05 | cm/cm/°C |
| Flow: 23 to 150 ° C | 23to150℃ | ISO 11359-2 | 3.9E-05 | cm/cm/°C |
| Horizontal: -40 to 40 ° C | Across Flow, -40to40℃ | ASTME831 | 9E-05 | cm/cm/°C |
| Across Flow, -40to40℃ | ISO 11359-2 | 7E-05 | cm/cm/°C | |
| 1.8MPa, unannealed, 3.20mm | ASTM D648 | 115 | °C | |
| 0.45MPa, unannealed, 64.0mm span | ISO 75-2/Bf | 135 | °C | |
| 0.45MPa, unannealed, 3.20mm | ASTM D648 | 175 | °C | |
| Horizontal: 23 to 80 ° C | Across Flow, 23to80℃ | ISO 11359-2 | 9E-05 | cm/cm/°C |
| Horizontal: 23 to 150 ° C | Across Flow, 23to150℃ | ISO 11359-2 | 1.5E-04 | cm/cm/°C |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| density | ASTMD792 | 1.31 | g/cm³ | |
| melt mass-flow rate | 200°C/3.8kg | ASTM D1238 | 18 | g/10min |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO 62 | 0.10 | % |
| Saturation,23°C | ISO 62 | 0.15 | % | |
| Shrinkage rate | TD2 | Internal Method | 0.50-0.90 | % |
| MD:3.20mm | Internal Method | 0.40-0.60 | % | |
| melt mass-flow rate | 265°C/5.0kg | ASTM D1238 | 85 | g/10min |
| Shrinkage rate | MD1 | Internal Method | 0.30-0.80 | % |
| Melt Volume Flow Rate (MVR) | 265°C/5.0kg | ISO 1133 | 75.0 | cm3/10min |
| 250°C/5.0kg | ISO 1133 | 50.0 | cm3/10min | |
| 250°C/2.16kg | ISO 1133 | 18.0 | cm3/10min | |
| melt mass-flow rate | 266°C/5.0kg | ASTM D1238 | 85 | g/10min |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| 1MHz | 1MHz | ASTMD150 | 3.10 | |
| 60Hz | 60Hz | IEC 60250 | 3.00 | |
| 100Hz | 100Hz | IEC 60250 | 3.20 | |
| 50Hz | 50Hz | IEC 60250 | 3.00 | |
| Hot wire ignition | HWI | UL 746 | PLC 0 | |
| High arc combustion index | HAI | UL 746 | PLC 0 | |
| Compared to the anti leakage trace index | SolutionB | IEC 60112 | PLC 4 | |
| 100Hz | 100Hz | IEC 60250 | 0.016 | |
| Compared to the anti leakage trace index | -- | IEC 60112 | PLC 3 | |
| 60Hz | 60Hz | IEC 60250 | 9E-03 | |
| 50Hz | 50Hz | IEC 60250 | 9E-03 | |
| 1MHz | 1MHz | ASTMD150 | 0.014 | |
| 3.20mm, in oil | IEC 60243-1 | 18 | KV/mm | |
| 1.60mm, in oil | IEC 60243-1 | 25 | KV/mm | |
| 0.800mm, in oil | IEC 60243-1 | 29 | KV/mm | |
| 3.20mm, inoil | ASTM D149 | 18 | KV/mm | |
| 1.60mm,inOil | ASTM D149 | 25 | KV/mm | |
| 0.800mm,inOil | ASTM D149 | 29 | KV/mm | |
| Volume resistivity | ASTMD257 | >1.0E+15 | ohms·cm | |
| Surface resistivity | IEC 60093 | >1.0E+15 | ohms | |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | R-Sale | ISO 2039-2 | 122 | |
| Ball Pressure Test | H358/30 | ISO 2039-1 | 165 | Mpa |
| Supplementary Information | Test Condition | Test Method | Test Result | Test Unit |
| Filling material | ASTM D229 | 10 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.