Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133 | 7.0 g/10min |
| Melt volume flow rate | | ISO 1133 | 6.00 cm3/10min |
| Shrinkage rate | | ISO 294-4 | 1.7 % |
| Shrinkage rate | | ISO 294-4 | 2.0 % |
| Water absorption rate | | ISO 62 | 0.60 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO 2039-2 | 70 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ColorNumber | | | CF2001/CD3501 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Wear factor | | JISK7218 | 16 10^-8mm³/N·m |
| Wear factor | | JISK7218 | 400 10^-8mm³/N·m |
| Wear factor | | JISK7218 | 900 10^-8mm³/N·m |
| Tensile modulus | | ISO 527-2 | 2700 Mpa |
| tensile strength | | ISO 527-2 | 50.0 Mpa |
| Nominal tensile fracture strain | | ISO 527-2 | 20 % |
| Flexural modulus | | ISO 178 | 2500 Mpa |
| bending strength | | ISO 178 | 75.0 Mpa |
| | JISK7218 | 0.21 |
| | JISK7218 | 0.14 |
| Wear factor | | JISK7218 | <1.0 10^-8mm³/N·m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC 60093 | 2E+14 ohms·cm |
| dielectric strength | | IEC 60243-1 | 18 KV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Hot deformation temperature (HDT) | | ISO 75-2/A | 80.0 °C |
| | 内部方法 | 1.1E-04 cm/cm/°C |
| | 内部方法 | 1.1E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.