MS TX-100S DENKA JAPAN

Form：Granules | Grade：Injection grade

Properties:

Weather resistancetransparent

Typical Applications:

CastersOptical level

Supplier(1)

Product Description

Certificates(0)

Datasheet

Alternative(4)

Product Description

Typical Applications:	Casters \| Optical level
Properties:	Weather resistance \| transparent

Certificates

No Data...

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			具有与有机玻璃同样良好的透明性、耐气候性、表面强度、而且比有机玻璃树脂更有吸湿率比重小以及成型性好的聚合物
purpose			光学镜片.灯具罩.停车场棚架等有关外围设备
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
density	23℃	ISO 1183	1.127	kg/cm3
Total Light Transmittance	2mmt	ISO 13468-1	92	%
turbidity	2mmt	ISO 14762	0.2	%
Rockwell hardness	23℃	ISO 2039-2	86	(M)
mobility	200℃，49N，Flow性	ISO 1133	2.0	g/10分
mobility	mobility	200℃，98N，Flow性	ISO 1133	26	g/10分
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus		ASTM D790/ISO 178	3.320	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	111	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	86
bending strength	2mm/min	ISO 178	111	Mpa
Tensile stress	5mm/min，Break	ISO 527-1	73	Mpa
Charpy Notched Impact Strength	Notched,23℃	ISO 179	2	kJ/m²
Bending modulus	2mm/min	ISO 178	3.320	Mpa
Tensile strain	5mm/min，Break	ISO 527-1	6	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Combustibility (rate)		UL 94	HB
Vicat softening temperature		ASTM D1525/ISO R306	100	℃（℉）
Vicat softening temperature	Vicat softening temperature	50N荷重	ISO 306	100	%
Combustibility		UL 94	HB
Hot deformation temperature	1.8MPa应力	ISO 75-1	78	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density			1.127

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.