Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt viscosity | | ISO 11443 | 220 Pa·s |
| density | | ISO 1183 | 1.38 g/cm³ |
| Shrinkage rate | | ISO 294-4 | 0.70to1.3 % |
| Shrinkage rate | | ISO 294-4 | 0.10to0.40 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 7.5 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 6000 MPa |
| tensile strength | | ISO 527-2 | 100 MPa |
| Tensile strain | | ISO 527-2 | 2.8 % |
| Flexural modulus | | ISO 178 | 5300 MPa |
| bending strength | | ISO 178 | 150 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1E+13 ohms |
| Volume resistivity | | IEC 60093 | 1E+14 ohms·cm |
| dielectric strength | | IEC 60243-1 | 20 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 160 °C |
| melting temperature | | ISO 11357-3 | 225 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.