PET UmaPET ITM
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTM D1204 | 2.2 % | |
| ASTM D1204 | 2.2 % | ||
| ASTM D1204 | 0 % | ||
| ASTMD1204 | 2.2 % | ||
| ASTMD1204 | 2.2 % | ||
| ASTMD1204 | 0.0 % | ||
| ASTMD1204 | 0.0 % | ||
| Surface tension Metallizedside | ASTMD2578 | 56 mN/m | |
| ASTMD2578 | 56 mN/m | ||
| Shrinkage rate | ASTM D1204 | 0 % |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Optical Density | 内部方法 | -2.8到7.2 % | |
| 内部方法 | -2.8到7.2 % |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| oxygen permeability | ASTMD3985 | <0.800 cm³/m²/24hr | |
| ASTMD3985 | <0.700 cm³/m²/24hr | ||
| Water vapor permeability | ASTMF1249 | <0.60 g/m²/24hr | |
| ASTMF1249 | <0.70 g/m²/24hr | ||
| usage | 内部方法 | 59.5 m²/kg | |
| 内部方法 | 31.0 m²/kg | ||
| tensile strength | ASTMD882 | 196 MPa | |
| ASTMD882 | 226 MPa | ||
| ASTMD882 | 206 MPa | ||
| elongation | ASTMD882 | 100 % | |
| Film thickness - tested | 1223 µm | ||
| Available film thickness | 12,23µm | ||
| tensile strength | ASTMD882 | 216 MPa | |
| elongation | ASTMD882 | 100 % | |
| ASTMD882 | 95 % | ||
| ASTMD882 | 95 % |
| film properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation | ASTM D882 | 95 % | |
| usage | Internal Method | 59.5 m²/kg | |
| Internal Method | 31 m²/kg | ||
| Water vapor permeability | ASTM F1249 | ＜0.60 g/m²/24 hr | |
| ASTM F1249 | ＜0.70 g/m²/24 hr | ||
| Optical Density | Internal Method | -2.8 到 7.2 % | |
| Internal Method | -2.8 到 7.2 % | ||
| Film thickness - tested | 12，23 µm | ||
| Available film thickness | 12，23 µm | ||
| tensile strength | ASTM D882 | 216 MPa | |
| ASTM D882 | 196 MPa | ||
| ASTM D882 | 226 MPa | ||
| ASTM D882 | 206 MPa | ||
| elongation | ASTM D882 | 100 % | |
| ASTM D882 | 100 % | ||
| ASTM D882 | 95 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.