PPA HFFR-4133 BK318 SOLVAY USA

Form：Granules | Grade：Injection grade

Properties:

Low warpageGlass fiber reinforcedFiller: Glass fiber reinf33% filler by weightcharacteristicUltra high impact20% glass fiber reinforce

Typical Applications:

Automotive ApplicationsElectrical componentsElectrical/Electronic ApplicationsLaptop caseAxial flow fan blades for air conditioningCentrifugal fan bladeCross-flow fan motor boardphotographic equipmentInstrument frameworkAutomotive parts

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Automotive Applications \| Electrical components \| Electrical/Electronic Applications \| Laptop case \| Axial flow fan blades for air conditioning \| Centrifugal fan blade \| Cross-flow fan \| motor board \| photographic equipment \| Instrument framework \| Automotive parts
Properties:	Low warpage \| Glass fiber reinforced \| Filler: Glass fiber reinf \| 33% filler by weight \| characteristic \| Ultra high impact \| 20% glass fiber reinforce

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength		ISO 180/1U	40to48	kJ/m²
Impact strength of cantilever beam gap		ISO 180/1A	7.0to8.0	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.40mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Yield	ISO 527-2	145to160	Mpa
Tensile strain	Break	ISO 527-2	1.9to2.3	%
Tensile modulus		ISO 527-2	12000	Mpa
Bending modulus		ISO 178	10800	Mpa
bending strength		ISO 178	220to230	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/Af	300	°C
Linear coefficient of thermal expansion	MD:0to90°C	ASTME831	2E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD:120to200°C	ASTME831	1.2E-05	cm/cm/°C
		Linear coefficient of thermal expansion	TD:0to90°C	ASTME831	8E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:120to200°C	ASTME831	1.3E-04	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	TD	ISO 294-4	1.3	%
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.32	%
Water absorption rate	24hr	ASTM D570	0.28	%
density		ISO 1183/A	1.46	g/cm³
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric strength	0.800mm	ASTM D149	30	KV/mm
Dielectric strength	Dielectric strength	1.60mm	ASTM D149	26	KV/mm
Dielectric constant	100Hz	ASTM D150	3.78
Dielectric constant	Dielectric constant	1MHz	ASTM D150	3.53
Dissipation factor	100Hz	ASTM D150	5E-03
Dissipation factor	Dissipation factor	1MHz	ASTM D150	0.012
Compared to the anti leakage trace index	CTI	UL 746	PLC 0
Volume resistivity		ASTM D257	1.3E+16	ohms·cm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	121

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.