Technical Data Sheet
| other | Test Condition | Test Method | Test Result |
|---|
| | | 30%玻璃纤维增强.热稳定.注塑成型 |
| Color | | | 本色/黑色 |
| processability | Test Condition | Test Method | Test Result |
|---|
| Dry conditions | | | 75-85°C / 2-4h |
| Temperature | | | 90-100 °C °C |
| Melt Temperature | | | 240-270 °C °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256/ISO 179 | 80 kg·cm/cm(J/M)ft·lb/in |
| Impact strength of cantilever beam gap | | ASTM D256/ISO 179 | 15 kg·cm/cm(J/M)ft·lb/in |
| elongation at break | | ASTM D638/ISO 527 | 180 % |
| Tensile modulus | | ASTM D638/ISO 527 | 9500 kg/cm²(MPa)[Lb/in²] |
| Rockwell hardness | | ASTM D785 | 122 |
| Flexural modulus | | ASTM D790/ISO 178 | 8500 kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 270 kg/cm²(MPa)[Lb/in²] |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 1.36 |
| Shrinkage rate | | ASTM D955 | 0.3-0.5 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTM D257/IEC 60093 | 1013 Ω |
| Volume resistivity | | ASTM D257/IEC 60093 | 101⁵ Ω.cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Hot deformation temperature (HDT) | | ASTM D648/ISO 75 | 200 ℃（℉） |
| melting temperature | | | 221 ℃（℉） |
| vicat | | ASTM D1525/ISO R306 | 215 ℃（℉） |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.