ABS

ABS NP2H-AT BK LANXESS THAI

Properties:
Anti static
Compare View Prices

Technical Data Sheet

Other performance	Test Condition	Test Method	Test Result
gloss	60°		93

mechanical properties	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	-20℃	ISO 180/1A	- kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23℃	ISO 180/1A	17 kJ/m²
melt mass-flow rate	220℃；10kg	ISO 1133	37 g/10min
Rockwell hardness	t=6.4mm	ISO 2039-2	111 R标尺
Elongation at Break	50mm/min	ISO 527	20 %
Bending modulus	2mm/min 80×10×4	ISO 178	2300 Mpa
Tensile modulus	1mm/min	ISO 527	2400 Mpa
tensile strength	50mm/min	ISO 527	33 Mpa
Tensile stress	50mm/min，Yield	ISO 527	43 Mpa
bending strength	2mm/min 80×10×4	ISO 178	68 Mpa

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature	50N:120K/h	ISO 306	94 °C
UL flame retardant rating	1.6mm	UL 94	HB 类别

Physical properties	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45Mpa	ISO 75	- °C
density		ISO 1183	1.05 g/cm³
Hot deformation temperature	1.80Mpa	ISO 75	- °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.