EAA PRIMACOR™ 3004 STYRON US
702
- Properties:Heat sealing performanceHigh toughnessResistance to stress crac
- Usages:Electric wireCable
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 190℃/2.16kg | ASTM D-1238 | 8.5 | g/10min |
| 190℃/2.16kg | ISO 1133 | 8.5 | g/10min | |
| Monomer content | % | |||
| density | ASTM D-792 | g/cm³ | ||
| ISO 1183 | g/cm³ | |||
| ASTMD792,ISO1183 | 0.938 | g/cm³ | ||
| Melt mass flow rate | 190°C/2.16kg | ASTMD1238,ISO1133 | 8.5 | g/10min |
| Content of comonomer | 9.7 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | 屈服,模压成型 | ASTMD638,ISO527-2 | 7.93 | Mpa |
| 断裂,模压成型 | ASTMD638,ISO527-2 | 17.6 | Mpa | |
| elongation | 断裂,模压成型 | ASTMD638,ISO527-2 | 600 | % |
| Tensile yield strength | Compression Molded | ASTM D-638 | Mpa | |
| Compression Molded | ISO 527-2 | Mpa | ||
| Tensile fracture strength | Compression Molded | ASTM D-638 | Mpa | |
| Compression Molded | ISO 527-2 | Mpa | ||
| Tensile strain at break | Compression Molded | ASTM D-638 | 600 | % |
| Compression Molded | ISO 527-2 | 600 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| vicat softening point | ASTMD1525,ISO306 | 81.1 | °C | |
| Melting temperature | 内部方法 | 98.0 | °C | |
| vicat softening point | ASTM D-1525 | ℃ | ||
| ISO 306 | ℃ |
| Processing conditions | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Temperature | ℃ | 260-290 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.