Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.97 g/cm³ |
| Shrinkage rate | | | 0.50 % |
| Shrinkage rate | | | 0.20 % |
| Water absorption rate | | ISO62 | 0.020 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO2039-2 | 101 |
| Rockwell hardness | R-Scale | ISO2039-2 | 120 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ISO527-2 | 145 MPa |
| Tensile strain | Break | ISO527-2 | 0.90 % |
| Flexural modulus | | ISO178 | 22000 MPa |
| Bending stress | | ISO178 | 245 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO180/A | 13 kJ/m² |
| | ISO180 | 25 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | UL746 | 250 V |
| Volume resistivity | | ASTMD257 | 1E+15 ohms·cm |
| dielectric strength | | IEC60243-1 | 16 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO11359-2 | 1.5E-04 cm/cm/°C |
| | ISO11359-2 | 3E-04 cm/cm/°C |
| | ISO11359-2 | 7E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO11359-2 | 0.59 W/m/K |
| | ISO75-2/A | >260 °C |
| | ISO11359-2 | 1.5E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.