PA66 U4820L NC01 INVISTA SHANGHAI

146

Form：Granules

Properties:

ProcessabilitycurrencyLubricityFast forming cycleColor stabilityGood demolding performanc

Typical Applications:

Electrical fieldElectronic fieldAutomotive sectorHousehold appliancesHousehold appliancescurrency

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electrical field \| Electronic field \| Automotive sector \| Household appliances \| Household appliances \| currency
Properties:	Processability \| currency \| Lubricity \| Fast forming cycle \| Color stability \| Good demolding performanc

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179	NoBreak
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning wire flammability index	3.0mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	0.71mm	IEC 60695-2-13	960	°C
	Hot filament ignition temperature	1.5mm	IEC 60695-2-13	900	°C
	Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC 60695-2-13	750	°C
UL flame retardant rating	0.40mm	UL 94	V-2
Burning wire flammability index	0.71mm	IEC 60695-2-12	960	°C
Burning wire flammability index	Burning wire flammability index	1.5mm	IEC 60695-2-12	960	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2/1	3200	Mpa
tensile strength	Yield	ISO 527-2/50	82.0	Mpa
Tensile strain	Yield	ISO 527-2	4.1	%
Tensile strain	Tensile strain	Break	ISO 527-2	35	%
Bending modulus		ISO 178	3000	Mpa
bending strength		ISO 178	96.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	221	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	71.0	°C
Melting temperature		ISO 11357-3	262	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	TD:2.00mm	ISO 294-4	1.8	%
Shrinkage rate	Shrinkage rate	MD:2.00mm	ISO 294-4	1.8	%
Water absorption rate	23°C,24hr	ISO 62	1.7	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	3E+14	ohms
Volume resistivity	2.00mm	IEC 60093	4E+14	ohms·cm
Dielectric strength	1.00mm	IEC 60243-1	32	KV/mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.