Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTMD1238 | 5.5 g/10min |
| melt mass-flow rate | | ISO1133 | 5.7 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTMD785 | 110 |
| Rockwell hardness | | ISO2039-2 | 110 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2/50 | 2300 Mpa |
| tensile strength | | ASTMD638 | 41.0 Mpa |
| tensile strength | | ISO527-2/50 | 42.0 Mpa |
| tensile strength | | ISO527-2/50 | 33.0 Mpa |
| Tensile strain | | ISO527-2/50 | 14 % |
| Flexural modulus | | ASTMD790 | 2200 Mpa |
| Flexural modulus | | ISO178 | 2200 Mpa |
| bending strength | | ASTMD790 | 61.0 Mpa |
| bending strength | | ISO178 | 62.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam gap 6 | | ISO179/1eA | 16 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 88.0 °C |
| | ASTMD648 | 100 °C |
| | ISO75-2/A | 75.0 °C |
| | ISO75-2/A | 95.0 °C |
| vicat | | ISO306/B50 | 97.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.