Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
density | | ASTM D792 | 1.45 g/cm³ |
Water absorption rate | | ASTM D570 | 0.30 % |
Water absorption rate | Saturation | ASTM D570 | 1.5 % |
hardness | Test Condition | Test Method | Test Result |
---|
Rockwell hardness | M-Scale | ASTM D785 | 106 |
Shore hardness | | ASTM D2240 | 90 |
Rockwell hardness | | ASTM D785 | 70 |
flammability | Test Condition | Test Method | Test Result |
---|
UL flame retardant rating | | UL 94 | V-0 |
Supplementary Information | Test Condition | Test Method | Test Result |
---|
limiting pv value | | 内部方法 | 0.788 MPa·m/s |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
compressive strength | | ASTM D695 | 110 MPa |
coefficient of friction | Steel - Static | 内部方法 | 0.20 |
Tensile modulus | | ASTM D638 | 3030 MPa |
tensile strength | Ultimate | ASTM D638 | 68.9 MPa |
elongation | Break | ASTM D638 | 3.0 % |
Flexural modulus | | ASTM D790 | 4480 MPa |
bending strength | Yield | ASTM D790 | 138 MPa |
Compression Modulus | | ASTM D695 | 2480 MPa |
Wear factor | | ASTM D3702 | 9.1 10^-8mm³/N·m |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Impact strength of cantilever beam gap | | ASTM D256A | 27 J/m |
Electrical performance | Test Condition | Test Method | Test Result |
---|
Surface Resistivity | | 内部方法 | >1.0E+13 ohms |
dielectric constant | | ASTM D150 | 6.00 |
Dissipation Factor | | ASTM D150 | 0.042 |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Heat distortion temperature | | ASTM D648 | 279 °C |
Maximum operating temperature LongTerm, Air | | | 260 °C |
Glass Transition Temperature | | ASTM D3418 | 275 °C |
Linear coefficient of thermal expansion | | ASTME831 | 3.6E-05 cm/cm/°C |
thermal conductivity | | ASTMF433 | 0.53 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.