Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Resin | | 按重量计算的混合比:100按容量计算的混合比:100 |
| Hardener | | 按重量计算的混合比:100按容量计算的混合比:89 |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| density | | | 1.08到1.12 g/cm³ |
| | | 0.040到0.050 Pa·s |
| Curing Time | | | 0.25到0.50 hr |
| STORAGE STABILITY | | | 1.5到2.5 min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO7619 | 70到74 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ISO178 | 1400到1600 MPa |
| Bending stress | | ISO178 | 52.0到62.0 MPa |
| compression stress | | ISO604 | 40.0到50.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179 | 20到28 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 82.0到88.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.