Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238, ISO 1133 | 4.0 g/10 min |
| melt mass-flow rate | | ASTM D1238, ISO 1133 | 40 g/10 min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 105 |
| Rockwell hardness | | ISO 2039-2 | 105 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638, ISO 527-2 | 43.0 Mpa |
| Flexural modulus | | ASTM D790, ISO 178 | 2450 Mpa |
| bending strength | | ASTM D790, ISO 178 | 75.0 Mpa |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 70 到 80 °C |
| drying time | | | 2.0 到 3.0 hr |
| Processing (melt) temperature | | | 180 到 230 °C |
| Temperature | | | 40 到 80 °C |
| Injection Pressure | | | 58.8 到 108 Mpa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Thermal deformation temperature under load | | ASTM D648, ISO 75-2/A | 84.0 °C |
| Thermal deformation temperature under load | | ASTM D648, ISO 75-2/A | 94.0 °C |
| vicat | | ISO 306/A, ASTM D15254 | 100 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.