PP AP3N EXXONMOBIL SINGAPORE

Form：Granules | Grade：Injection grade

Properties:

High rigidityHigh glossMiddle flowFast forming cycle

Typical Applications:

Electrical appliancesHome appliance componentsConsumer goods sectorConsumer product application field

Supplier(1)

Product Description

Certificates(2)

Datasheet

Product Description

Typical Applications:	Electrical appliances \| Home appliance components \| Consumer goods sector \| Consumer product application field
Properties:	High rigidity \| High gloss \| Middle flow \| Fast forming cycle

Certificates

TDS

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-20°C	ISO 179/1eA	4.0	kJ/m²
	Charpy Notched Impact Strength	0°C	ISO 179/1eA	4.5	kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	8.6	kJ/m²
Impact strength of cantilever beam gap	23°C	ASTM D256A	96	J/m
	Impact strength of cantilever beam gap	-40°C	ISO 180/1A	3.8	kJ/m²
		Impact strength of cantilever beam gap	-18°C	ISO 180/1A	4.5	kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	8.3	kJ/m²
Dart impact	-29°C,3.18mm	ASTM D5420	18.0	J
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	3.6	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2/1	1690	Mpa
tensile strength	Yield3	ASTM D638	28.8	Mpa
tensile strength	tensile strength	Yield	ISO 527-2/50	28.2	Mpa
elongation	Yield3	ASTM D638	5.0	%
elongation	elongation	Yield	ISO 527-2/50	5.0	%
Bending modulus	1%Secant4	ASTM D790A	1480	Mpa
	Bending modulus	1%Secant5	ASTM D790B	1710	Mpa
	Bending modulus	Bending modulus	--6	ISO 178	1510	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	114	°C
	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/Bf	100	°C
		Hot deformation temperature	0.45MPa,Annealed	ASTM D648	123	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	54.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	230°C/2.16kg	ASTM D1238	10	g/10min
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness		ASTM D785	98

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.