ABS VH-0815 LOTTE CHEM DONGGUAN

Form：Granules | Grade：Injection grade

Properties:

Flame retardantHigh impact resistance

Typical Applications:

Electronic fieldElectrical field

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electronic field \| Electrical field
Properties:	Flame retardant \| High impact resistance

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C	ISO 180/1A	19	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	22	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	2.0mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	1.5mm	UL 94	V-1
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile strain	Break	ISO 527-2/50	8.0	%
Bending modulus		ASTM D790	2200	Mpa
elongation	Break	ASTM D638	17	%
tensile strength	Break	ISO 527-2/50	33.0	Mpa
	tensile strength	Break	ASTM D638	27.0	Mpa
		tensile strength	Yield	ISO 527-2/50	45.0	Mpa
		tensile strength	tensile strength	Yield	ASTM D638	39.0	Mpa
Tensile modulus		ISO 527-2/50	2200	Mpa
Tensile modulus	Tensile modulus		ASTM D638	2000	Mpa
bending strength		ISO 178	71.0	Mpa
bending strength	bending strength		ASTM D790	59.0	Mpa
Bending modulus		ISO 178	2400	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature	--	ISO 306/B120	88.0	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	86.0	°C
Hot deformation temperature	1.8MPa,Annealed,4.00mm	ISO 75-2/A	79.0	°C
	Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/A	71.0	°C
		Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	77.0	°C
			Hot deformation temperature	0.45MPa,Annealed,4.00mm	ISO 75-2/B	84.0	°C
			Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ISO 75-2/B	81.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	200°C/5.0kg	ASTM D1238	3.8	g/10min
Shrinkage rate	MD:3.20mm	ISO 2577	0.34-0.41	%
melt mass-flow rate	200°C/5.0kg	ISO 1133	4.2	g/10min
Shrinkage rate	MD：3.20mm	ASTM D955	0.34-0.41	%
	Shrinkage rate	TD：3.20mm	ASTM D955	0.36-0.44	%
	Shrinkage rate	Shrinkage rate	TD:3.20mm	ISO 2577	0.36-0.44	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ISO 2039-2	104
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	100

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.