Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.19 g/cm³ |
| Water absorption rate | | ASTM D570 | 0.50 % |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTM D2457 | 161 |
| refractive index | | ASTM D542 | 1.550 |
| transmissivity | | ASTM D1003 | 92.0 % |
| Haze ratio | | ASTM D1003 | 0.70 % |
| Yellowness Index | | ASTM D1925 | 0.50 YI |
| UV Transmittance | | | 89 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| SurfaceEnergy | | ASTM D5946 | 46 dyne/cm |
| SurfaceEnergy | | ASTM D5946 | 39 dyne/cm |
| SurfaceEnergy | | ASTM D5946 | 8 dyne/cm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Abrasion | | ASTM D1044 | 23haze % |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tear strength | | ASTM D1938 | 12 kN/m |
| tear strength | | ASTM D1938 | 13 kN/m |
| film | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D882 | 40.0 MPa |
| tensile strength | | ASTM D882 | 59.0 MPa |
| tensile strength | | ASTM D882 | 52.0 MPa |
| elongation | | ASTM D882 | 7.0 % |
| elongation | | ASTM D882 | 7.0 % |
| elongation | | ASTM D882 | 180 % |
| Water Vapor Transmission Rate | | ASTMF1249 | 4.0 g/m²/24hr |
| Water Vapor Transmission Rate | | ASTMF1249 | 11 g/m²/24hr |
| Carbon dioxide transmittance | | ASTM D1434 | 150 cm³·mm/m²/atm/24hr |
| Elmendorf tear strength | | ASTM D1922 | 5 N |
| Elmendorf tear strength | | | 6 N |
| PPTTearResistance | | ASTM D2582 | 42 N |
| PPTTearResistance | | ASTM D2582 | 56 N |
| tear strength | | ASTM D1938 | 410 gf |
| tear strength | | ASTM D1938 | 310 gf |
| film thickness | | | 250 µm |
| Thin film puncture strength | | ASTM D3763 | 4.60 J |
| Secant modulus | | ASTM D882 | 1500 MPa |
| Secant modulus | | ASTM D882 | 1400 MPa |
| tensile strength | | ASTM D882 | 41.0 MPa |
| Tear resistance of pants | | ISO 6383-1 | 11.0 N/mm |
| OTr | | ASTM D3985 | 32 cm³·mm/m²/atm/24hr |
| elongation | | ASTM D882 | 200 % |
| Dart impact | | ASTM D1709A | 910 g |
| Dart impact | | ASTM D1709A | 880 g |
| Tear resistance of pants | | ISO 6383-1 | 11.0 N/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| specific heat | | DSC | 1700 J/kg/°C |
| specific heat | | DSC | 1900 J/kg/°C |
| specific heat | | DSC | 2200 J/kg/°C |
| specific heat | | DSC | 2400 J/kg/°C |
| specific heat | | DSC | 2600 J/kg/°C |
| melting temperature | | | 110 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 9E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.