'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PC 201R-111 SABIC INNOVATIVE US
133
Form：Granules | Grade：Injection grade
Properties:
High glossHigh temperature resistan
Typical Applications:
Automotive componentselectronic product
Product Description
Certificates(0)
Datasheet
Alternative(3)
Product Description
| Typical Applications: | Automotive components | electronic product |
| Properties: | High gloss | High temperature resistan |
Certificates
No Data...
Technical Data Sheet
| optical performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Refractive index | ASTM D542 | 1.586 | ||
| transmissivity | 2540 μm | ASTM D1003 | 88.0 | % |
| turbidity | 2540 μm | ASTM D1003 | 1.0 | % |
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
| Impact strength of cantilever beam gap | ASTM D1822 | 630 | kJ/m² | |
| Dart impact | 23°C | ASTM D3029 | 169 | J |
| 23°C, Energy at Peak | ASTM D3763 | 64.0 | J | |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 3200 | J/m |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 1.1 mm | UL 94 | V-2 | |
| 6.0 mm | UL 94 | V-0 | ||
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Taber abraser | 1000 Cycles, 1000 g, CS-17 Wheel | ASTM D1044 | 10.0 | mg |
| bending strength | Yield, 50.0 mm Span | ASTM D790 | 97.0 | Mpa |
| Bending modulus | 50.0 mm Span | ASTM D790 | 2340 | Mpa |
| elongation | Break | ASTM D638 | 140 | % |
| Yield | ASTM D638 | 7.0 | % | |
| tensile strength | Break | ASTM D638 | 68.0 | Mpa |
| Yield | ASTM D638 | 62.0 | Mpa | |
| injection | Test Condition | Test Method | Test Result | Test Unit |
| Mold temperature | 80 to 115 | °C | ||
| Back pressure | 0.300 to 0.700 | Mpa | ||
| drying temperature | 120 | °C | ||
| drying time | 3.0 to 4.0 | hr | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Suggested injection volume | 40 to 60 | % | ||
| Temperature at the rear of the barrel | 290 to 310 | °C | ||
| Temperature in the middle of the barrel | 300 to 320 | °C | ||
| Temperature at the front of the material cylinder | 310 to 330 | °C | ||
| Spray nozzle temperature | 305 to 325 | °C | ||
| Processing (melt) temperature | 310 to 330 | °C | ||
| Screw speed | 40 to 70 | rpm | ||
| Exhaust hole depth | 0.025 to 0.076 | mm | ||
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| RTI Imp | UL 746 | 130 | °C | |
| RTI | UL 746 | 130 | °C | |
| RTI Elec | UL 746 | 130 | °C | |
| thermal conductivity | ASTM C177 | 0.29 | W/m/K | |
| specific heat | ASTM C351 | 1250 | J/kg/°C | |
| Linear coefficient of thermal expansion | -40 to 95°C，Flow | ASTM E831 | 6.8E-5 | cm/cm/°C |
| Vicat softening temperature | ASTM D15255 | 154 | °C | |
| Hot deformation temperature | 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 132 | °C |
| 0.45 MPa, Unannealed, 6.40 mm | ASTM D648 | 137 | °C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Specific volume | ASTM D792 | 0.830 | cm³/g | |
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 7.0 | g/10 min |
| Shrinkage rate | 3.20 mm，Flow | Internal Method | 0.50 - 0.70 | % |
| Outdoor applicability | UL 746C | f2 | ||
| Water absorption rate | Equilibrium, 100°C | ASTM D570 | 0.58 | % |
| Equilibrium, 23°C | ASTM D570 | 0.35 | % | |
| 24 hr | ASTM D570 | 0.15 | % | |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Volume resistivity | ASTM D257 | > 1.0E+17 | ohms·cm | |
| Dielectric strength | 3.20 mm, in Air | ASTM D149 | 15 | KV/mm |
| Dielectric constant | 60 Hz | ASTM D150 | 3.17 | |
| 50 kHz | ASTM D150 | 3.17 | ||
| 1 MHz | ASTM D150 | 2.96 | ||
| Dissipation factor | 50 Hz | ASTM D150 | 9.0E-4 | |
| 60 Hz | ASTM D150 | 9.0E-4 | ||
| 1 MHz | ASTM D150 | 0.010 | ||
| Compared to the anti leakage trace index | UL 746 | PLC 2 | ||
| High arc combustion index | UL 746 | PLC 1 | ||
| High voltage arc tracing rate | UL 746 | PLC 2 | ||
| Hot wire ignition | UL 746 | PLC 2 | ||
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | R-Scale | ASTM D785 | 118 | |
| M-Scale | ASTM D785 | 70 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.