Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.29 g/cm³ |
| Water absorption rate | | ASTMD570 | 1.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Limiting Oxygen Index | | ASTMD2863 | 23 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Break | ASTMD638 | 95.0 MPa |
| elongation | Break | ASTMD638 | 6.0 % |
| Flexural modulus | | ASTMD790 | 5400 MPa |
| fracture | | ASTM D790 | 180 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ASTM D256 | 46.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179 | 46 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTMD257 | 1E+15 ohms·cm |
| dielectric strength | | ASTMD149 | 34 kV/mm |
| Solution A | | IEC 60112 | 450 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | ASTM D696 | 3E-05 cm/cm/°C |
| melting temperature | | ASTMD2117 | 260 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.