Technical Data Sheet
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| Color | | | Clear/Transparent |
| density | | | 1.15 g/cm³ |
| Color | | | Amber |
| density | | | 1.22 g/cm³ |
| density | | | 0.15to0.30 Pa·s |
| density | | | 1.0 hr |
| density | Pot Life | | 1400 min |
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Thermosetting components | | | 按重量计算的混合比:1.0 |
| Thermosetting components | | | 按重量计算的混合比:1.0 |
| Thermosetting components | | | 52 wk |
| physical property | Test Condition | Test Method | Test Result |
|---|
| Ionic type | | | 22 ppm |
| Ionic type | | | 26 ppm |
| Ionic type | | | 3 ppm |
| Ionic type | | | 15 ppm |
| Cured Properties | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | | 67 |
| LapShearStrength | | | 10.0 MPa |
| relative permittivity | | | 3.36 |
| Volume resistivity | | | >1.0E+13 ohms·cm |
| Dissipation Factor | | | 5E-03 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | | >98.0 % |
| refractive index | | | 1.520 |
| transmissivity | | | >90.0 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| DegradationTemperature | | | 375 °C |
| Shear Strength | | | 23.4 MPa |
| operate temperature | | | <300 °C |
| StorageModulus | | | 2.58 GPa |
| weight loss on heating | | | 0.060 % |
| weight loss on heating | | | 0.17 % |
| weight loss on heating | | | 0.50 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | | 2.1E-04 cm/cm/°C |
| Glass Transition Temperature | | | >95.0 °C |
| Linear coefficient of thermal expansion | | | 5.7E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.