PA6 6G40

43
  • Properties:
    Glass fiber reinforced
    Filler: Glass fiber reinf
    40% filler by weight
  • Usages:
    Automotive sector
    Electronic field
    Electrical field

Technical Data Sheet

physical property Test ConditionTest MethodTest Result
Shrinkage rateISO 25770.70-0.90 %
Shrinkage rateISO 25770.20-0.40 %
viscosity numberISO 307145 cm³/g
flammabilityTest ConditionTest MethodTest Result
burning rateFMVSS302<100 mm/min
UL flame retardant ratingUL 94HB
Mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulusISO 527-2/113000 Mpa
tensile strength ISO 527-2/5200 Mpa
Tensile strainISO 527-2/52.5 %
Flexural modulusISO 17810500 Mpa
bending strengthISO 178280 Mpa
Impact resistanceTest ConditionTest MethodTest Result
Impact strength of simply supported beam without notchISO 179/1eU110 kJ/m²
Suspended wall beam without notch impact strengthISO 180/1U95 kJ/m²
Electrical performanceTest ConditionTest MethodTest Result
Surface ResistivityIEC 600931E+13 ohms
Volume resistivityIEC 600931E+15 ohms·cm
Thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature (HDT)ISO 75-2/B220 °C
Hot deformation temperature (HDT)ISO 75-2/A200 °C
vicatISO 306/B50215 °C
melting temperatureISO 11357-3222 °C
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.