PPO(PPE)+PS Jamplast JPPPO30GF Jamplast, Inc.

Properties:

Filler glass fiber reinforced material 20% filler by weight

Typical Applications:

Pump components casing valves valve parts

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Pump components \| casing \| valves \| valve parts
Properties:	Filler \| glass fiber reinforced material \| 20% \| filler by weight

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	-40°C	ASTM D256	96	J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D256	120	J/m
Suspended wall beam without notch impact strength	23°C	ASTM D256	650	J/m
Dart impact	23°C,TotalEnergy	ASTM D3763	22.6	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	HB
Extreme Oxygen Index		ASTM D2863	26	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ASTM D638	6200	MPa
tensile strength	Break	ASTM D638	90.3	MPa
elongation	Break	ASTM D638	2.6	%
Bending modulus	50.0mmSpan	ASTM D790	5800	MPa
bending strength	Yield,50.0mmSpan	ASTM D790	160	MPa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	141	°C
RTI Imp		UL 746	90.0	°C
RTI		UL 746	90.0	°C
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	2.9E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	8.3E-05	cm/cm/°C
RTI Elec		UL 746	90.0	°C
Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	143	°C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	135	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	138	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792	1.20	g/cm³
melt mass-flow rate	300°C/5.0kg	ASTM D1238	9.0	g/10min
Shrinkage rate	MD：3.20mm	ASTM D955	0.20to0.50	%
Water absorption rate	24hr	ASTM D570	0.060	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric strength	3.20mm,inOil	ASTM D149	17	kV/mm
Dielectric constant	50Hz	ASTM D150	2.86
High voltage arc tracing rate	HVTR	UL 746	PLC 4
Hot wire ignition	HWI	UL 746	PLC 4
Dielectric constant	60Hz	ASTM D150	2.86
Dissipation factor	50Hz	ASTM D150	8E-04
Dissipation factor	Dissipation factor	60Hz	ASTM D150	8E-04
Arc resistance		ASTM D495	PLC7
High arc combustion index	HAI	UL 746	PLC 4
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	L-Sale	ASTM D785	106

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.