PA66 101F DUPONT USA

142

Form：Granules | Grade：Special level

Properties:

High slidingwear resistant

Typical Applications:

Electrical fieldElectronic fieldEngine parts

Supplier(1)

Product Description

Certificates(1)

Datasheet

Alternative(2)

Product Description

Typical Applications:	Electrical field \| Electronic field \| Engine parts
Properties:	High sliding \| wear resistant

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	4.5	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	6.0	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	400	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap	-40°C	ISO 180/1A	5.5	kJ/m²
	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	6.0	kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	5.5	kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	300	kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	300	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	V-2
	UL flame retardant rating	0.71mm	IEC 60695-11-10,-20	V-2
	UL flame retardant rating	UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	V-2
Extreme Oxygen Index		ISO 4589-2	28	%
FMVSS flammability		FMVSS302	SE
Fogging-G-value	condensate	ISO 6452	1E-04	g
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile creep modulus	1hr	ISO 899-1	--	Mpa
Tensile creep modulus	Tensile creep modulus	1000hr	ISO 899-1	--	Mpa
Bending modulus		ISO 178	2800	Mpa
Tensile modulus		ISO 527-2	3100	Mpa
tensile strength	Yield	ISO 527-2	82.0	Mpa
Tensile strain	Yield	ISO 527-2	4.5	%
Nominal tensile fracture strain		ISO 527-2	20	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Effective thermal diffusivity coefficient			5E-08	m²/s
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	190	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	70.0	°C
Glass transition temperature		ISO 11357-2	60.0	°C
Vicat softening temperature		ISO 306/B50	240	°C
Melting temperature		ISO 11357-3	262	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	1E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	1.1E-04	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
MediumDensity			0.970	g/cm³
Top out temperature			190	°C
SpecificHeatCapacity of Melt			2790	J/kg/°C
ThermalConductivityofMelt			0.16	W/m/K
density		ISO 1183	1.14	g/cm³
Shrinkage rate	TD	ISO 294-4	1.4	%
	Shrinkage rate	TD:80°C,48hr	ISO 294-4	0.10	%
		Shrinkage rate	MD	ISO 294-4	1.4	%
		Shrinkage rate	Shrinkage rate	MD:80°C,48hr	ISO 294-4	0.20	%
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	8.5	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	2.6	%
Stickiness		ISO 307	140	cm³/g
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		IEC 60093	1E+15	ohms·cm
Dielectric strength		IEC 60243-1	32	KV/mm
Relative permittivity	100Hz	IEC 60250	3.80
Relative permittivity	Relative permittivity	1MHz	IEC 60250	3.60
Dissipation factor	100Hz	IEC 60250	0.014
Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.018
film	Test Condition	Test Method	Test Result	Test Unit
Tensile strain	Yield，MD	ISO 527-3	4.5	%
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
EmissionofOrganicCompounds		VDA277	6.50	µgC/g
Odor		VDA270	3.00

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.