PC ML7672-111 SABIC EU

Form：Granules | Grade：Injection grade

Properties:

High temperature resistanFlame retardantFiller: Glass fiber reinf

Typical Applications:

Electronic and electrical accessoriesAutomotive componentsCasters

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Electronic and electrical accessories \| Automotive components \| Casters
Properties:	High temperature resistan \| Flame retardant \| Filler: Glass fiber reinf

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
23°C		ASTM D256	240	J/m
Charpy Notched Impact Strength	23°C	ISO 179/1eA	19	kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	28.2	J
23°C		ISO 180/1A	19	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
crack		ASTM D638	52.0	Mpa
yield		ISO 527-2/5	11.0	Mpa
--1		ASTM D638	5200	Mpa
Yield, 50.0mm span		ASTM D790	99.0	Mpa
--6		ISO 178	100	Mpa
--5		ISO 178	5480	Mpa
50.0mm span		ASTM D790	4860	Mpa
crack		ISO 527-2/5	1.8	%
crack	crack		ASTM D638	5.0	%
yield		ISO 527-2/5	0.30	%
crack		ISO 527-2/5	57.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	6.9E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	2.7E-05	cm/cm/°C
1.8MPa, unannealed, 64.0mm span of		ISO 75-2/Af	140	°C
1.8MPa, unannealed, 3.20mm		ASTM D648	138	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.30	%
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.20	%
Shrinkage rate	MD：3.20mm	Internal Method	0.20-0.60	%
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	5.00	cm3/10min
melt mass-flow rate	300°C/1.2kg	ASTM D1238	4.5	g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.