Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | | 1.50 g/cm³ |
| Shrinkage rate | | | 0.30 % |
| Shrinkage rate | | | 0.10 % |
| Water absorption rate | Equilibrium | ASTM D570 | 0.040 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 91 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 11500 MPa |
| tensile strength | | ASTM D638 | 170 MPa |
| elongation | | ASTM D638 | 2.0to3.0 % |
| Flexural modulus | | ASTM D790 | 11.9 MPa |
| bending strength | | ASTM D790 | 260 MPa |
| compressive strength | | ASTM D695 | 167 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 60 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 610 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 372 °C |
| Continuous use temperature | | UL 746B | 300 °C |
| Glass Transition Temperature | | ASTM D3418 | 176 °C |
| melting temperature | | ASTM D3418 | 396 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.