PC/ABS DN-7730M JIAXING TEIJIN

Form：Granules | Grade：Injection grade

Properties:

Flame retardantHigh rigidityBromine freeFiller: Mineral fillerfillerMineral fillerfiller30%Filler is rigid by weightHigh bromine free flame r

Typical Applications:

Industrial applicationsBusiness equipmentBusiness equipmentIndustrial applicationsBusiness equipmentIndustrial applicationsIndustrial applicationsBusiness equipment

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Industrial applications \| Business equipment \| Business equipment \| Industrial applications \| Business equipment \| Industrial applications \| Industrial applications \| Business equipment
Properties:	Flame retardant \| High rigidity \| Bromine free \| Filler: Mineral filler \| filler \| Mineral filler \| filler \| 30% \| Filler is rigid by weight \| High bromine free flame r

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength		ISO 179	3.0	kJ/m²
Impact strength of simply supported beam without notch		ISO 179	18	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2/1	9000	Mpa
tensile strength	Break	ISO 527-2/5	66.0	Mpa
Tensile strain	Break	ISO 527-2/5	2.0	%
Bending modulus		ISO 178	8000	Mpa
bending strength		ISO 178	100	Mpa
Tensile modulus		ISO 527-2/1	9000	Mpa
tensile strength	Break	ISO 527-2/5	66	Mpa
Tensile strain	Break	ISO 527-2/5	2.0	%
Bending modulus		ISO 178	8000	Mpa
bending strength		ISO 178	100	Mpa
Charpy Notched Impact Strength		ISO 179	3	kJ/m²
Impact strength of simply supported beam without notch		ISO 179	18	kJ/m²
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	120	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	108	°C
Vicat softening temperature		ISO 306/B50	122	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	3.2E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	3.7E-05	cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	120	℃
	Hot deformation temperature	热变形温度，1.80MPa,Unannealed	ISO 75-2/A	108	℃
		Hot deformation temperature	维卡软化温度	ISO 306/B50	122	℃
			Hot deformation temperature	线形热膨胀系数，Flow	ISO 11359-2	3E-05	cm/cm/℃
			Hot deformation temperature	Hot deformation temperature	线形热膨胀系数，Across Flow	ISO 11359-2	3.5E-05	cm/cm/℃
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.40	g/cm³
Shrinkage rate	TD:4.00mm	Internal Method	0.20-0.40	%
Shrinkage rate	Shrinkage rate	MD:4.00mm	Internal Method	0.10-0.30	%
density		ISO 1183	1.4	g/m3
Shrinkage rate	TD：4.00mm	Internal Method	0.2-0.4	%
Shrinkage rate	Shrinkage rate	MD：4.00mm	Internal Method	0.1-0.3	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	1E+16	ohms
Surface resistivity	Surface resistivity		IEC 60093	1E+16	ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.