Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | JISK6922-1 | 0.50 g/10min |
| Environmental stress cracking resistance | | JISK6760-1981 | >1000 hr |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | JISK7215 | 49 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | JISK7105 | 115 |
| Haze ratio | | ASTM D1003 | 4.0 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | | JISK7113 | 850 % |
| Flexural modulus | | ASTM D747-70 | 130 Mpa |
| tensile strength | | JISK7113 | 30.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D1822 | 1160 kJ/m² |
| film | Test Condition | Test Method | Test Result |
|---|
| Secant modulus | | 内部方法 | 110 Mpa |
| Secant modulus | | 内部方法 | 130 Mpa |
| tensile strength | | JISK6781 | 32.0 Mpa |
| tensile strength | | JISK6781 | 34.0 Mpa |
| elongation | | JISK6781 | 550 % |
| elongation | | JISK6781 | 710 % |
| Dart impact | | ASTM D1709A | 74 g |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | JISK72062 | 90.0 °C |
| melting temperature | | DSC | 102 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.