Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| STORAGE STABILITY | | | 1400 min |
| stripping time | | | 20 min |
| stripping time | | | 10 min |
| Post curing time | | | 16to24 hr |
| Post curing time | | | 16to24 hr |
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.18 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 60 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Wear factor | | | 144 |
| Wear factor | | | 203 |
| Wear factor | | | 1100 % |
| Wear factor | | | 1600 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Wear factor | | | 100 mm³ |
| Wear factor | | | 71.0 mm³ |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D412 | 17.6 MPa |
| tensile strength | | ASTM D412 | 17.9 MPa |
| tensile strength | | ASTM D412 | 30.6 MPa |
| tensile strength | | ASTM D412 | 31.4 MPa |
| tensile strength | | ASTM D412 | 37.7 MPa |
| tensile strength | | ASTM D412 | 37.9 MPa |
| elongation | | ASTM D412 | 300 % |
| Falling ball impact strength | | | 47 % |
| Shore hardness | | ASTM D2632 | 45 % |
| Falling ball impact strength | | | 47 % |
| elongation | | ASTM D412 | 330 % |
| tear strength | | ASTM D624 | 98.1 kN/m |
| tear strength | | ASTM D624 | 99.8 kN/m |
| tear strength | | ASTM D470 | 22 kN/m |
| tear strength | | ASTM D470 | 25 kN/m |
| compression set | | ASTM D395A | 5.0 % |
| compression set | | ASTM D395A | 3.0 % |
| compression set | | ASTM D395A | 8.0 % |
| compression set | | ASTM D395A | 5.0 % |
| Shore hardness | | ASTM D2632 | 45 % |
| film | Test Condition | Test Method | Test Result |
|---|
| Tear resistance of pants | | ASTM D1938 | 40.3 N/mm |
| Tear resistance of pants | | ASTM D1938 | 42.0 N/mm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.