TPEE 4068 DUPONT USA

Form：Granules | Grade：Injection grade

Properties:

Thermal stabilityAging resistance

Typical Applications:

Castersmedical care

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Casters \| medical care
Properties:	Thermal stability \| Aging resistance

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap	23°C	ISO 8256/1	145	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning rate	1.00mm	ISO 3795	<100	mm/min
FMVSS flammability		FMVSS302	B
elastomer	Test Condition	Test Method	Test Result	Test Unit
tear strength	Flow	ISO 34-1	100	kN/m
tear strength	tear strength	横向Flow	ISO 34-1	100	kN/m
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2	45.0	Mpa
Wear resistance		ISO 4649	180	mm³
Bending modulus		ISO 178	45.0	Mpa
Tensile creep modulus	1000hr	ISO 899-1	21.0	Mpa
Tensile creep modulus	Tensile creep modulus	1hr	ISO 899-1	28.0	Mpa
Nominal tensile fracture strain		ISO 527-2	800	%
Tensile strain	Break	ISO 527-2	>300	%
tensile strength	100%Strain	ISO 527-2	7.50	Mpa
	tensile strength	50%Strain	ISO 527-2	6.70	Mpa
		tensile strength	Break	ISO 527-2	29.0	Mpa
			tensile strength	5.0%Strain	ISO 527-2	2.40	Mpa
			tensile strength	tensile strength	10%Strain	ISO 527-2	3.20	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Glass transition temperature		ISO 11357-2	-55.0	°C
Melting temperature		ISO 11357-3	193	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	2.3E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	2.3E-04	cm/cm/°C
Effective thermal diffusivity coefficient			5.44E-08	m²/s
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.30	%
	Water absorption rate	Saturation,23°C,2.00mm	ISO 62	0.70	%
	Water absorption rate	Water absorption rate	23°C,24hr	ISO 62	0.70	%
Shrinkage rate	MD	ISO 294-4	0.80	%
Shrinkage rate	Shrinkage rate	TD	ISO 294-4	0.80	%
Melt Volume Flow Rate (MVR)	220°C/2.16kg	ISO 1133	8.80	cm3/10min
ThermalConductivityofMelt			0.16	W/m/K
SpecificHeatCapacity of Melt			2140	J/kg/°C
MediumDensity			1.03	g/cm³
melt mass-flow rate	220°C/2.16kg	ISO 1133	8.5	g/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric strength		IEC 60243-1	18	KV/mm
Relative permittivity	100Hz	IEC 60250	4.80
Relative permittivity	Relative permittivity	1MHz	IEC 60250	4.70
hardness	Test Condition	Test Method	Test Result	Test Unit
Shore hardness	ShoreD,15Sec	ISO 868	33
Shore hardness	Shore hardness	ShoreD	ISO 868	37
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
Odor		VDA270	4.00
EmissionofOrganicCompounds		VDA277	10.0	µgC/g

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.