'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
LCP A130-VF3001 CELANESE USA
149
Form：Granules | Grade：Injection grade
Properties:
Flame retardantGlass fiber reinforcedThermal stabilityChemical resistance
Typical Applications:
Electrical fieldElectronic fieldHousehold appliancesHousehold appliances
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | Electrical field | Electronic field | Household appliances | Household appliances |
| Properties: | Flame retardant | Glass fiber reinforced | Thermal stability | Chemical resistance |
Certificates
No Data...
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 29 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | UL 94 | V-0 | ||
| Extreme Oxygen Index | ISO 4589-2 | 45 | % | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Tensile creep modulus | 1000 hr | ISO 899-1 | 10900 | Mpa |
| 1 hr | ISO 899-1 | 12600 | Mpa | |
| Compressive stress | 1% Strain | ISO 604 | 100 | Mpa |
| Compressive modulus | ISO 604 | 14500 | Mpa | |
| bending strength | 23°C | ISO 178 | 280 | Mpa |
| Bending modulus | 23°C | ISO 178 | 14500 | Mpa |
| Tensile strain | Break | ISO 527-2/1A/5 | 2.1 | % |
| tensile strength | Break | ISO 527-2/1A/5 | 190 | Mpa |
| Tensile modulus | ISO 527-2/1A | 15000 | Mpa | |
| injection | Test Condition | Test Method | Test Result | Test Unit |
| Hopper temperature | 20 to 30 | °C | ||
| drying temperature | 150 | °C | ||
| drying time | 4.0 to 6.0 | hr | ||
| Suggested maximum moisture content | 0.010 | % | ||
| Temperature at the rear of the barrel | 270 to 280 | °C | ||
| Temperature in the middle of the barrel | 275 to 285 | °C | ||
| Temperature at the front of the material cylinder | 280 to 290 | °C | ||
| Spray nozzle temperature | 290 to 300 | °C | ||
| Processing (melt) temperature | 285 to 295 | °C | ||
| Mold temperature | 80 to 120 | °C | ||
| Injection speed | 快速 | |||
| Back pressure | < 3.00 | Mpa | ||
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Linear coefficient of thermal expansion | Across Flow | ISO 11359-2 | 2.3E-5 | cm/cm/°C |
| Flow | ISO 11359-2 | 6.0E-6 | cm/cm/°C | |
| Melting temperature | ISO 11357-3 | 280 | °C | |
| Vicat softening temperature | ISO 306/B50 | 160 | °C | |
| Hot deformation temperature | 8.0 MPa, Unannealed | ISO 75-2/C | 190 | °C |
| 1.8 MPa, Unannealed | ISO 75-2/A | 235 | °C | |
| 0.45 MPa, Unannealed | ISO 75-2/B | 250 | °C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Water absorption rate | Equilibrium, 23°C, 50% RH | ISO 62 | 0.040 | % |
| Shrinkage rate | Flow | ISO 294-4 | 0.20 | % |
| 横向Flow | ISO 294-4 | 0.40 | % | |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Relative permittivity | 100 Hz | IEC 60250 | 4.20 | |
| 1 MHz | IEC 60250 | 3.70 | ||
| Dissipation factor | 100 Hz | IEC 60250 | 0.016 | |
| 1 MHz | IEC 60250 | 0.018 | ||
| Dielectric strength | IEC 60243-1 | 31 | KV/mm | |
| Volume resistivity | IEC 60093 | 1.0E+15 | ohms·cm | |
| Surface resistivity | IEC 60093 | > 1.0E+15 | ohms | |
| Arc resistance | Internal Method | 140 | sec | |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | M -Sale | ISO 2039-2 | 85 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.