TP, Unspecified GS 2189 Germany BIOTEC
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ISO 1133 | 15to40 g/10min | |
| Particle size | 2.00to3.00 mm | ||
| density | ISO 1183 | 1.20to1.40 g/cm³ | |
| Apparent density | ISO 60 | 0.88to0.94 g/cm³ |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 75 kJ/m² | |
| ISO 179 | 140 kJ/m² |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt density | ISO 1133 | 1.10to1.30 g/cm³ |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Carbon dioxide transmittance | ASTM D1434 | 150to200 cm³/m²/24hr | |
| oxygen permeability | ASTMF1927 | 40.0to60.0 cm³/m²/24hr | |
| film thickness | ISO 2286-3 | >10 µm | |
| tensile strength | DIN 53455 | 40.0to50.0 MPa | |
| DIN 53455 | 35.0to45.0 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ISO 306/A120 | 60.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.