Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.68 g/cm³ |
| Water absorption rate | | ASTM D570 | <0.10 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 75 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ASTM D790 | 1690 MPa |
| Impact strength of cantilever beam gap | | ASTM D256 | NB J/m |
| tensile strength | | ASTM D638 | 29.6 MPa |
| tensile strength | | ASTM D638 | 53.8 MPa |
| elongation at break | | ASTM D638 | 5.0 % |
| elongation at break | | ASTM D638 | 250 % |
| Tensile modulus | | ASTM D638 | 1650 MPa |
| bending strength | | ASTM D790 | 46.9 MPa |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|
| Limiting Oxygen Index | | ASTM2863 | 56 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTM D149 | 79 KV/mm |
| dielectric constant | | ASTM D150 | 2.50 1kHz |
| Dissipation Factor | | ASTM D150 | 1.6E-03 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 90 °C |
| Heat distortion temperature | | ASTM D648 | 62.8 °C |
| vicat | Melting Temperature | | 240 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 1E-04 cm/cm／°C |
| Linear coefficient of thermal expansion | | | 149 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.