Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183/A | 1.18 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO7619 | 75 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179 | NoBreak |
| Charpy Notched Impact Strength | | ISO179 | NoBreak |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Wear amount | | ISO4649-A | 50.0 mm³ |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | Yield | DIN53504 | 40.0 MPa |
| elongation | | DIN53504 | 800 % |
| elongation | Break | DIN53504 | 900 % |
| tear strength | | ISO34-1 | 50 kN/m |
| compression set | | ISO815 | 25 % |
| compression set | | ISO815 | 35 % |
| compression set | | ISO815 | 50 % |
| tensile strength | | DIN53504 | 2.00 MPa |
| Tensile stress | | DIN53504 | 3.50 MPa |
| Tensile stress | | DIN53504 | 6.00 MPa |
| Tensile stress | Yield | DIN53504 | 35.0 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO306/A120 | 100 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.