PA+PPO(PPE) KumhoSunny PA/PPE HAP8920
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.10 g/cm³ | |
| melt mass-flow rate | ISO 1133 | 70 g/10min | |
| Shrinkage rate | ISO 294-4 | 1.1to1.5 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 无断裂 | |
| Charpy Notched Impact Strength | ISO 179 | 25 kJ/m² | |
| ISO 179 | 9.7 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO 179 | 无断裂 | |
| Impact strength of cantilever beam gap | ISO 180 | 7.9 kJ/m² | |
| ISO 180 | 18 kJ/m² | ||
| Suspended wall beam without notch impact strength | ISO 180 | 无断裂 | |
| ISO 180 | 无断裂 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ISO 527-2/50 | 63.0 MPa | |
| Tensile strain | Break | ISO 527-2/50 | 80 % |
| Flexural modulus | ISO 178 | 2200 MPa | |
| bending strength | ISO 178 | 75.0 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| Surface Resistivity | IEC 60093 | 1E+15 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/B | 175 °C | |
| ISO 75-2/A | 110 °C | ||
| vicat | ISO 306/B50 | 190 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 9E-05 cm/cm/°C | |
| ISO 11359-2 | 1.3E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.