PC/ABS PC-365KB ZHENJIANG CHIMEI

153

Form：Granules

Properties:

Flame retardantheat-resistingHigh impact resistance

Typical Applications:

Electrical applicationsAutomotive Applicationscurrency

Supplier(2)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electrical applications \| Automotive Applications \| currency
Properties:	Flame retardant \| heat-resisting \| High impact resistance

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179	45	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180	50	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179	50	kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180	45	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus	23°C	ASTM D790	2260	Mpa
Bending modulus	Bending modulus		ISO 178	2200	Mpa
bending strength	23°C	ASTM D790	78.5	Mpa
bending strength	bending strength		ISO 178	80.0	Mpa
Tensile strain	Break	ISO 527-2/50	120	%
Tensile strain	Tensile strain	Break,23°C	ASTM D638	85	%
tensile strength	Break	ISO 527-2/50	50.0	Mpa
	tensile strength	Yield	ISO 527-2/50	54.0	Mpa
	tensile strength	tensile strength	Yield,23°C	ASTM D638	53.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	8E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	8E-05	cm/cm/°C
Vicat softening temperature	--	ISO 306/B50	127	°C
	Vicat softening temperature	--	ISO 306/A50	138	°C
		Vicat softening temperature	--	ASTM D152511	125	°C
		Vicat softening temperature	Vicat softening temperature	--	ASTM D152510	136	°C
Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/A	102	°C
	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	115	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	106	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate		ISO 2577	0.40-0.60	%
Shrinkage rate	Shrinkage rate	MD	ASTM D955	0.40-0.60	%
Spiral flow length		Internal Method	30.0	CM
melt mass-flow rate	260°C/5.0kg	ISO 1133	20	g/10min
melt mass-flow rate	melt mass-flow rate	260°C/5.0kg	ASTM D1238	20	g/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric constant	1MHz	IEC 60250	3.10
Volume resistivity		IEC 60093	1E+18	ohms·cm
Surface resistivity		IEC 60093	1E+16	ohms
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Sale,23°C	ISO 2039-2	115
Rockwell hardness	Rockwell hardness	R-Sale,23°C	ASTM D785	115

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PC/ABS PC-365KB ZHENJIANG CHIMEI

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index