Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 0.960 g/cm³ |
| density | | ISO 1183 | 0.960 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 1.0 g/10min |
| melt mass-flow rate | | ISO 1133 | 1.0 g/10min |
| IonType | | | Zinc |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 61 |
| Shore hardness | | ISO 868 | 61 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| Haze ratio | | ASTM D1003 | 12 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ASTM D790 | 250 MPa |
| wear resistance | | ASTM D1630 | 410 |
| tensile strength | | ASTM D638 | 11.7 MPa |
| tensile strength | | ASTM D638 | 10.3 MPa |
| tensile strength | | ISO 527-2 | 10.3 MPa |
| elongation | | ASTM D638 | 440 % |
| Tensile strain | | ISO 527-2 | 440 % |
| Flexural modulus | | ASTM D790 | 717 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D1822 | 1040 kJ/m² |
| Impact strength of cantilever beam gap | | ASTM D1822 | 1260 kJ/m² |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tear strength | | ASTM D624 | 1.02 kN/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| brittle temperature | | ASTM D746 | -110 °C |
| vicat | | ASTM D1525 | 71.0 °C |
| vicat | | ISO 306 | 71.0 °C |
| melting temperature | | ASTM D3418 | 92.0 °C |
| melting temperature | | ISO 3146 | 92.0 °C |
| FreezingPoint | | ASTM D3418 | 76 °C |
| FreezingPoint | | ISO 3146 | 76 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.